EFFECTS OF HYBRIDIZATION OF PALM KERNEL FIBRE AND SNAIL SHELL FILLER ON SOME END-USE PROPERTIES OF EPOXY-BASED COMPOSITES
Keywords:
Composite, Hybridization, Impact strength, Palm kernel shell fibre, Snail shell fibreAbstract
This work studied the effects of hybridization of palm kernel shells fibre (PKF) and snail shells filler (SSF) on microstructural, mechanical, and water absorption properties of epoxy-based composites. Microstructure analysis of the composite samples was conducted using a digital optical microscope. Universal testing machine (UTM) was employed to evaluate the mechanical properties (tensile and compressive strengths) of the composite. Shore D hardness Durometer was used to evaluate the composite material's resistance to deformation, while Izod impact tester was deployed to determine the impact strength of the composites. The gravimetric technique was used to measure the water absorption by the composites. Results showed that the microstructures of the epoxy-based composite samples (8 – 10) with hybridized PKF and SSF fillers revealed improper mixing and non uniform distribution of the filler materials, particularly on samples 8 and 10, while sample 9 appear to be uniformly distributed. Further, sample 10 gave highest ultimate tensile strength of 12.721 MPa and impact strength of 0.211 J/mm2, while sample 9 displayed highest value of Young’s modulus of elasticity of 209.469 MPa, compared to the epoxy-based composites with mono fillers of PKF and SSF. The water absorption assessment showed that water absorption increased with increasing temperature
References
Achukwu E.O., Barnabas A M., Mamman A., Uzochukwu M.I. Fabrication of palm kernel shell epoxy composites and study of their mechanical properties, Nigerian Journal of Materials Science and Engineering, 2015, 6(1):32-38.
Baffour-Awuah E., Akinlabi S.A., Jen T.C., Hassan S., Okokpujie I.P., Ishola F. Characteristics of Palm Kernel Shell and Palm Kernel Shell-Polymer Composites: A Review, IOP Conf. Series: Materials Science and Engineering, 2021, 1107, 012090. doi:10.1088/1757-899X/1107/1/012090
Bello S.A., Agunsoye J.O., Hassan S.B., Zebase Kana M.G., Raheem I.A. Epoxy Resin Based Composites, Mechanical and Tribological Properties: A Review, Tribology in Industry, 2015, 37(4):500-524.
Demir O, Yar A, Eskizeybek V, Avcı A. Combined effect of fiber hybridization and matrix modification on mechanical properties of polymer composites. Proceedings of the Institution of Mechanical Engineers, Part L: Journal of Materials: Design and Applications. 2023;237(9):1935-1951. doi:10.1177/14644207231162547.
Kamo, Y. and Matsumoto, A. Stress relaxation and improved fracture toughness of metal bonding using flexible monolith sheets and an epoxy adhesive. Polym J. 2025, 57, 203–214. https://doi.org/10.1038/s41428-024-00975-w.
Kolawole M.Y., Aweda J.O., Abdulkareem S., Bello S.A., Ali A., Iqbal F. Influence of calcined snail shell particulates on mechanical properties of recycled aluminium alloy for automotive application. Journal of Acta Periodica Technologica, 2020, 51:163-180.
Oladele I.O, Ibrahim I.O, Adediran A.A., Akinwekomi A.D., Adetula Y.V., and Olayanju T.M.A. Modified palm kernel shell fiber/particulate cassava peel hybrid reinforced epoxy composites, Results in Materials, 5, 2020. https://doi.org/10.1016/j.rinma.2019.100053.
Olaitan A.J., Ufuoma O.D., King G.D. and Raphael O. Production of a safety helmet, palm kernel fibre and shell particulates, International Journal of Engineering Science Invention, 2017, 6(2):44-55.
Ramasamy B., Ramesh M., Ramanujam R., Sasikala G., Deepa C. Physical Properties of Glass-Hemp-Banana Hybrid Fiber Reinforced Polymer Composites, 2017 10(1), DOI: 10.17485/ijst/2017/v10i7/103310.
Sukanto H., Raharjo W.W., Ariawan D., Triyono J. and Kaavesina M. Epoxy resins thermosetting for mechanical engineering, Open Engineering, 2021, 11(1):797-814. https://doi.org/10.1515/eng-2021-0078
Valášek P., Habrová K., and Müller M., Experimental description of aging of palm oil kernel shell powder/epoxy composite, IOP Conf. Ser.: Mater. Sci. Eng., 2019:617. DOI 10.1088/1757-899X/617/1/012009.
Xu H., Zhang X., Yu Y., Yu Y., Weng L. Enhanced adhesion property of epoxy resin composites through dual reinforcement mechanisms, Next Materials, 2024, 3,100072. https://doi.org/10.1016/j.nxmate.2023.100072.
Zhang, J., Zhang, Z., Huang, R., and Tan, L. Advances in Toughening Modification Methods for Epoxy Resins: A Comprehensive Review. Polymers, 2025, 17(9), 1288. https://doi.org/10.3390/polym17091288